In vitro evaluation of coronal discoloration following the application of calcium-enriched mixture cement, Biodentine, and mineral trioxide aggregate in endodontically treated teeth


1 Department of Endodontics, Islamic Azad University, Dental Branch, Tehran, Iran
2 Department of Oral and Maxillofacial Radiology, Kermanshah University of Medical Sciences, Kermanshah, Iran
3 Department of Endodontics, Faculty of Dentistry, Kermanshah University of Medical Sciences, Kermanshah, Iran
4 Student Research Committee, Dental School, Kermanshah University of Medical Sciences, Kermanshah, Iran

Correspondence Address:
Dr. Mostafa Godiny
Department of Endodontics, Faculty of Dentistry, Kermanshah University of Medical Sciences, Kermanshah
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/1735-3327.249550

Rights and Permissions

Background: This study sought to assess and compare coronal discoloration following the application of white mineral trioxide aggregate, Biodentine, and calcium-enriched mixture cement in endodontically treated teeth. Materials and Methods: In this in vitro experimental study, 64 freshly extracted sound human premolars were selected, cleaned, and stored in saline. After cleaning, shaping, and obturation the root canal of the teeth, the teeth were randomly assigned to one control (n = 4) and three experimental (n = 20) groups. In the experimental groups, the cement were applied over the canal orifices in 3-mm thickness. All teeth were then restored with composite resin. Color parameters, according to the CIE L*a*b* system, were measured using Vita Easyshade spectrophotometer before application of cement and at 1 week, 1 month, 2 months, and 3 months after the application of cement. The recorded values were statistically analyzed using descriptive and analytical statistics. For analytical statistics, Kolmogorov–Smirnov test was applied to assess normal distribution of data. ANOVA was used to compare the results at baseline and repeated measures. P < 0.05 was considered statistically significant Results: Significant differences were noted in color change (ΔE) between all time points except between ΔE4 (2 months) and ΔE5 (3 months) (P < 0.01). However, tooth discoloration caused by the three cement was not significantly different (P = 0.343). Conclusion: The three tested cement were not significantly different in terms of causing coronal discoloration in endodontically treated teeth.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed286    
    Printed13    
    Emailed0    
    PDF Downloaded45    
    Comments [Add]    

Recommend this journal