ORIGINAL ARTICLE
Year : 2020  |  Volume : 17  |  Issue : 6  |  Page : 412-416

Fracture resistance of pulpotomized and composite-restored primary molars: Incremental versus bulk-fill techniques


1 Department of Pediatric Dentistry, Dental Research Center, Research Institute of Dental Science, Dental School, Shahid Beheshti University of Medical Sciences, Tehran, Iran
2 Department of Restorative Dentistry, Dental School, Shahid Beheshti University of Medical Sciences, Tehran, Iran
3 Department of Pediatric Dentistry, Dental School, Kermanshah University of Medical Sciences, Kermanshah, Iran
4 Department of Pediatric Dentistry, Dental School, Arak University of Medical Sciences, Arak, Iran

Date of Web Publication10-Dec-2020

Correspondence Address:
Dr. Khashayar Sanjari
Department of Pediatric Dentistry, Dental School, Arak University of Medical Sciences, Arak
Iran
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/1735-3327.302889

Rights and Permissions
  Abstract 


Background: The aim of this study was to assess the fracture resistance of pulpotomized primary molars restored with incremental and bulk-fill composite application techniques.
Materials and Methods: In this in-vitro experimental study, 36 extracted primary molars were nonrandomly (selectively) divided into three groups of 12 each. All teeth underwent conventional pulpotomy treatment, and mesio-occluso-distal cavities were prepared in such a way that the buccolingual width of the preparation was two-thirds of the intercuspal distance, and the depth of the buccal and lingual walls was 4 mm. The teeth were then restored as follows: Group 1 (control) was restored with amalgam, Group 2 was restored with Tetric N-Ceram composite using the incremental technique, and Group 3 was restored with Tetric N-Ceram composite using the bulk-fill technique. The restored teeth were subjected to thermocycling and then underwent fracture resistance testing in a universal testing machine at a crosshead speed of 1 mm/min. Fracture resistance of groups was compared using the one-way ANOVA and Tukey's honestly significant difference test.
Results: The mean fracture resistance was 1291.47 ± 603.88 N in the amalgam, 1283.08 ± 594.57 N in the Tetric N-Ceram incremental, and 1939.06 ± 134.47 N in the Tetric N-Ceram bulk-fill group. The difference in this regard between Group 3 and Groups 1 and 2 was statistically significant (P = 0.019 and P= 0.035, respectively).
Conclusion: Bulk-fill composite is recommended for reinforcing the remaining tooth structure after the primary molar pulpotomy procedure. Time-saving characteristics of this material are clinically important for reducing appointment time for children.

Keywords: Bulk-fill composite, conventional composite, fracture resistance, primary molar, pulpotomy


How to cite this article:
Ghajari MF, Ghasemi A, Moradi AY, Sanjari K. Fracture resistance of pulpotomized and composite-restored primary molars: Incremental versus bulk-fill techniques. Dent Res J 2020;17:412-6

How to cite this URL:
Ghajari MF, Ghasemi A, Moradi AY, Sanjari K. Fracture resistance of pulpotomized and composite-restored primary molars: Incremental versus bulk-fill techniques. Dent Res J [serial online] 2020 [cited 2021 Jan 24];17:412-6. Available from: https://www.drjjournal.net/text.asp?2020/17/6/412/302889




  Introduction Top


Dental caries in primary dentition is one of the most common diseases in children worldwide. Pulp therapy is necessary in cases with considerable tooth caries.[1] When primary molars undergo pulpotomy, their fracture resistance minimizes because of extensive loss of tooth structure.[2] Due to the undeniable importance of time required for the restoration of primary teeth, materials and techniques enabling a suitable restoration in the shortest time possible are high on demand.[3] When different treatment approaches exist for the restoration of primary teeth, clinicians choose a treatment based on procedures that are cost-effective and evidence-based.[4] Restoration of choice in these teeth is the stainless steel crown because tooth is preserved from fracture, leakage chance decreased, and provided a biological seal.[5] Although amalgam usage in the dental practice is diminished recently, due to its advantages such as low price, high durability, and being user-friendly, most dentists utilize it as their first choice for filling primary molar teeth.[6] Because of improved properties and good appearance, resin-based composites are introduced as a useful restorative material in dental practice.[7] There are some disadvantages in use of conventional composite resins. For example, they have to be used incrementally in 2-mm thick layers. Furthermore, the shrinkage associated with polymerization reaction can accumulate stress in tooth structure and lead to cusp deflection, bond failure, and finally failure of restoration.[8] A new generation in composite resins is presented to decrease the chair time of the conventional restorative procedure.[9] The “bulk-fill” composite introduced to decrease the polymerization shrinkage stress (major disadvantage of composite resin). Hence, this material can be used in a single layer (up to 4 mm), it is an alternative to restorations in the dental practice.[10] When the practitioner inserts this material in a single layer, the time required to accomplish the procedure can be lessened, thus contamination risk alleviated and longevity of restoration enhanced.[11] This study aimed to assess the fracture resistance of pulpotomized primary molars restored with amalgam and composite using the conventional incremental and bulk-fill techniques.


  Materials and Methods Top


This in-vitro, an experimental study was conducted on 36 extracted human primary second molars with the following inclusion criteria:

  • A minimum of one-third of the root remaining and intact furcation
  • The width of occlusal caries did not exceed one-third of the intercuspal distance
  • Caries depth on the gingival floor at the proximal surfaces had 2-mm distance from the cemento-enamel junction (CEJ).


All teeth were immersed in 1% chloramine-T solution at room temperature after collection until the experiment. The buccal and lingual dimensions of the crown (height and width) were measured by a digital caliper (serial number: 0020536/Mitutoyo, Japan) with 0.01 mm accuracy. To calculate tooth height, the sum of the distance between the palatal cusp tip and the CEJ and the buccal cusp tip and the CEJ was divided by two. Tooth size was calculated by dividing the tooth height by the tooth width. The selected teeth were nonrandomly and selectively divided into three groups of 12 equally based on their sizes. The teeth were prepared using diamond fissure burs with 1-mm diameter and 4-mm height (Jota, Switzerland) and high-speed handpiece underwater and air spray. First, the pulp chamber roof was removed, and then a mesio-occluso-distal cavity was prepared in such a way that the isthmus width of the occlusal cavity was two-thirds of the intercuspal distance, and the gingival floor in mesial and distal cavities was terminated at 1-mm distance from the CEJ. Using a periodontal probe (Hu-Friday, USA), the distance from the cavity preparation margin in the palatal wall and along the mesiopalatal cusp was measured to be 4 mm in such a way that after applying the reinforced zinc oxide cement (Zonalin Kemdent, England) and glass-ionomer cement (GC Fuji II Corporation, Tokyo), minimum thickness of composite in the pulp chamber cavity was 4 mm. Next, Zonalin paste was placed in the pulp chamber floor at 1-mm distance from the marked area for composite. A layer of glass-ionomer cement, mixed according to the manufacturer's instructions, was applied in 1-mm thickness. The cavities were restored as follows:

Group 1: cavities were filled with amalgam after placing a matrix band (Sinalux, Faghihi Co., Iran). Amalgam capsules were mixed in an amalgamator (Ultramat 2, SDI, and Australia) according to the manufacturer's instructions.

Group 2: cavities were etched with 37% phosphoric acid gel (Tetric N-Bond, Ivoclar Vivadent, Schaan, Liechtenstein) for 15 s, rinsed, and two layers of Tetric N-Bond (Ivoclar Vivadent, Schaan, Liechtenstein) was applied, and each layer was cured for 20 s using QTHART-L2 (Bonart Co., Taiwan) light-curing unit with a light intensity of 720 mW/cm2. Tetric N-Ceram conventional composite (Ivoclar Vivadent, Schaan, Liechtenstein) was applied incrementally. Three triangular-shaped oblique layers were applied in each of the mesial and distal cavities, and two triangular-shaped oblique layers were applied to the occlusal cavity. The thickness of each layer did not exceed 2 mm, and after applying, each layer was light-cured for 20 s.

Group 3: etching and bonding were performed as in Group 2. Tetris N-Ceram Bulk-Fill composite (Ivoclar Vivadent, Schaan, Liechtenstein) was placed in the cavities as bulk in such a way that the entire cavity was filled with composite and light-cured for 20 s using a quartz–tungsten–halogen light-curing unit.

Next, the specimens were immersed in distilled water for 1 week and were then subjected to thermocycling (1000 thermal cycles between 5°C and 55°C) (Dorsa, Iran). In the next step, the teeth were mounted in autopolymerizing acrylic resin in cylindrical molds measuring 3 cm in diameter and 3.5 cm in height at 2-mm distance from their CEJ. During the polymerization of the acrylic resin, the specimens were immersed in distilled water to decrease the heat generated from the acrylic polymerization and prevent dehydration of specimens. The specimens were then subjected to compressive stress in a universal testing machine (Zwick/Roell, Germany). The load applicator was semicircular with a diameter of 3.7 mm, and the loads were simultaneously applied to the buccal and palatal cusps. The load was applied at a crosshead speed of 1 mm/min vertical to the occlusal surface of teeth and increased until fracture.[10] The mode of failure of specimens was evaluated under a stereomicroscope at × 10. One-way ANOVA was used to compare the fracture resistance of groups. Tukey's honestly significant difference test was used for pair-wise comparison of groups.


  Results Top


Two specimens in the amalgam group were lost during the experiment. Descriptive statistics of the fracture resistance of the groups are shown in [Table 1].
Table 1: Descriptive statistics of the fracture resistance of groups (n=34)

Click here to view


Comparison of the fracture resistance values of specimens revealed statistically significant differences among groups (P = 0.012). The mean fracture resistance was 1291.47 ± 603.88 N in the amalgam, 1283.08 ± 594.57 N in the Tetric N-Ceram incremental, and 1939.06 ± 134.47 N in the Tetric N-Ceram Bulk-Fill group. The difference in this regard between Group 3 and Groups 1 and 2 was statistically significant (P = 0.019 and P = 0.035, respectively).


  Discussion Top


In vital teeth, the failure risk of restoration is less than the restorations which performed in pulpotomized teeth.[12] Resin composites, glass ionomers, or compomers are going to be more favorable than amalgam in operative dentistry of primary teeth.[13] To choose the most suitable material for filling primary pulpotomized molar, there is inadequate strong evidence. Resin composites could be pleasing in the matter of esthetics and also they can make bond to the structure of teeth.[14] Light-cure resin composites reduce the necessity to preparation of additional retention and they could set fast.[15] The depth of polymerization in light-cured resin composites is limited to 2 mm. The incomplete polymerization could cause depletion in mechanical and biological characteristics of composites. Bulk-fill composites are recommended to use in 4- or 5-mm increments. The use of the bulk-fill composites provides an easier restorative procedure and reduces the chair time in teeth with deep and wide cavities.[16] They could make the cusp strain and shrinkage stress lessen and raisen the fracture resistance.[17]

The present study aimed to evaluate the fracture resistance of pulpotomized primary second molars restored with amalgam and conventional incremental and bulk-fill composites. The results obtained in this study presented that within the study conditions; the fracture resistance of bulk-fill composite group was significantly higher than that of conventional composite and amalgam groups. Polymerization shrinkage in bulk-fill composites leads to a strain in tooth structure, which confronts the strain created by the compressive stresses that would result in tooth fracture. This can confer resistance to the remaining tooth structure against compressive stresses.[18],[19] On the other hand, different mechanisms prevent premature polymerization in bulk-fill composites such as the presence of stress-decreasing resin or shrinkage stress reliever fillers. Even the activity of fast initiators may be prevented in these composites resulting in a subsequent reduction in stress in the composite, this decreases the destructive behavior of conventional composites when applied as bulk.[20],[21] In a study by Malekafzali et al., similar to this study, fracture resistance of teeth restored with bulk-fill composite was increased and this finding has been confirmed in many previous studies.[22] Our findings are in agreement with Cobankara et al. who evaluated the fracture resistance of permanent premolars and reported the same results.[23] El-Kalla and García-Godoy, in their study on fracture resistance of pulpotomized primary molars, concluded that in comparison with amalgam, bonded restorations significantly increased the fracture resistance of primary molars.[7] Monga et al., in their study on endodontically treated premolars, showed that composite significantly increased the fracture resistance of teeth compared to amalgam; these results are in contrast to our findings.[24] This controversy may be attributed to the type of tooth, type of bonding agent used, type of composite, method of polymerization, the process of tooth restoration, and the remaining tooth structure after cavity preparation. Ehlers et al.[25] evaluated the performance of bulk-fill composites in the primary dentition. They declared that it is possible to mention bulk-fill materials as an alternative material in the restoration of primary teeth. Their results are similar to this study. Oter et al.[26] evaluated the performance of Class I cavities with bulk-fill composite for 1-year period. They figured out that bulk-fill composites could be performed in primary teeth with high rates of success. This result is in agreement with this study.

Based on the study of Taha et al.,[27] the fracture strength of restored teeth by bulk-fill resin composites was significantly higher than other groups and was close to a sound tooth. The result of this study is similar to the present study.

This study is based on extracted teeth and in-vitro condition. More clinical studies that specifically focus on fracture resistance of bulk-fill composites are definitely needed to confirm the clinical advantages of bulk-fill composites completely.


  Conclusion Top


The use of bulk-fill composite not only saves time but also significantly increases the fracture resistance of pulpotomized primary molars. Considering the above-mentioned advantages, bulk-fill composites are recommended for reinforcing the remaining tooth structure after pulpotomy treatment of primary molars.

Financial support and sponsorship

Nil.

Conflicts of interest

The authors of this manuscript declare that they have no conflicts of interest, real or perceived, financial or nonfinancial in this article.



 
  References Top

1.
Smaïl-Faugeron V, Courson F, Durieux P, Muller-Bolla M, Glenny AM, Fron Chabouis H, et al. Pulp treatment for extensive decay in primary teeth. Cochrane Database Syst Rev 2014 ;8:CD003220.  Back to cited text no. 1
    
2.
Alvanforoush N, Palamara J, Wong RH, Burrow MF. Comparison between published clinical success of direct resin composite restorations in vital posterior teeth in 1995-2005 and 2006-2016 periods. Aust Dent J 2017;62:132-45.  Back to cited text no. 2
    
3.
Mazhari F, Gharaghahi M. Effect of thickness of cavity wall on fracture strength of pulpotomized primary molar teeth with class II amalgam restorations. Eur Arch Paediatr Dent 2008;9:31-6.  Back to cited text no. 3
    
4.
Pires CW, Pedrotti D, Lenzi TL, Soares FZ, Ziegelmann PK, Rocha RO, et al. Is there a best conventional material for restoring posterior primary teeth? A network meta-analysis. Braz Oral Res 2018;32:e10.  Back to cited text no. 4
    
5.
Hutcheson C, Seale NS, McWhorter A, Kerins C, Wright J. Multi-surface composite vs. stainless steel crown restorations after mineral trioxide aggregate pulpotomy: A randomized controlled trial. Pediatr Dent 2012;34:460-7.  Back to cited text no. 5
    
6.
Vanishree HS, Shanthala BM, Bobby W. The comparative evaluation of fracture resistance and microleakage in bonded amalgam, amalgam, and composite resins in primary molars. Indian J Dent Res 2015;26:446-50.  Back to cited text no. 6
[PUBMED]  [Full text]  
7.
El-Kalla IH, García-Godoy F. Fracture strength of adhesively restored pulpotomized primary molars. ASDC J Dent Child 1999;66:238-42, 228.  Back to cited text no. 7
    
8.
Mosharrafian S, Heidari A, Rahbar P. Microleakage of two bulk fill and one conventional composite in class II restorations of primary posterior teeth. J Dent (Tehran) 2017;14:123-31.  Back to cited text no. 8
    
9.
van Dijken JW, Pallesen U. Randomized 3-year clinical evaluation of class I and II posterior resin restorations placed with a bulk-fill resin composite and a one-step self-etching adhesive. J Adhes Dent 2015;17:81-8.  Back to cited text no. 9
    
10.
Burgess J, Cakir D. Comparative properties of low-shrinkage composite resins. Compend Contin Educ Dent 2010;31 Spec No 2:10-5.  Back to cited text no. 10
    
11.
Olegário IC, Hesse D, Bönecker M, Imparato JC, Braga MM, Mendes FM, et al. Effectiveness of conventional treatment using bulk-fill composite resin versus atraumatic restorative treatments in primary and permanent dentition: A pragmatic randomized clinical trial. BMC Oral Health 2016;17:34.  Back to cited text no. 11
    
12.
Campagna P, Pinto LT, Lenzi TL, Ardenghi TM, de Oliveira Rocha R, Oliveira MD, et al. Survival and associated risk factors of composite restorations in children with early childhood caries: A clinical retrospective study. Pediatr Dent 2018;40:210-4.  Back to cited text no. 12
    
13.
Omidi BR, Naeini FF, Dehghan H, Tamiz P, Savadroodbari MM, Jabbarian R, et al. Microleakage of an enhanced resin-modified glass ionomer restorative material in primary molars. J Dent (Tehran) 2018;15:205-13.  Back to cited text no. 13
    
14.
Nematollahi H, Bagherian A, Ghazvini K, Esmaily H, Mehr MA. Microbial microleakage assessment of class V cavities restored with different materials and techniques: A laboratory study. Dent Res J (Isfahan) 2017;14:344-50.  Back to cited text no. 14
    
15.
Memarpour M, Derafshi R, Razavi M. Comparison of microleakage from stainless steel crowns margins used with different restorative materials: An in vitro study. Dent Res J (Isfahan) 2016;13:7-12.  Back to cited text no. 15
    
16.
Colak H, Ercan E, Hamidi MM. Shear bond strength of bulk-fill and nano-restorative materials to dentin. Eur J Dent 2016;10:40-5.  Back to cited text no. 16
[PUBMED]  [Full text]  
17.
Rosatto CM, Bicalho AA, Veríssimo C, Bragança GF, Rodrigues MP, Tantbirojn D, et al. Mechanical properties, shrinkage stress, cuspal strain and fracture resistance of molars restored with bulk-fill composites and incremental filling technique. J Dent 2015;43:1519-28.  Back to cited text no. 17
    
18.
Kim ME, Park SH. Comparison of premolar cuspal deflection in bulk or in incremental composite restoration methods. Oper Dent 2011;36:326-34.  Back to cited text no. 18
    
19.
Park J, Chang J, Ferracane J, Lee IB. How should composite be layered to reduce shrinkage stress: Incremental or bulk filling? Dent Mater 2008;24:1501-5.  Back to cited text no. 19
    
20.
Van Ende A, De Munck J, Van Landuyt KL, Poitevin A, Peumans M, Van Meerbeek B. Bulk-filling of high C-factor posterior cavities: Effect on adhesion to cavity-bottom dentin. Dent Mater 2013;29:269-77.  Back to cited text no. 20
    
21.
Sakaguchi RL, Powers JM. Craig's Restorative Dental Materials. 13th ed. Philadelphia: Elsevier Mobsy; 2012. p. 175.  Back to cited text no. 21
    
22.
Malekafzali B, Gassemi A, Mohtavipour S, Fotouhi Ardakani F, Goodarzi N, Fereydooni MR.In vitro investigation of the fracture strength of pulpotomized primary molars restored with glass ionomer, Amalgam and composite resin with and without cusp reduction. J Dent Sch Shahid Beheshti Univ Med Sci 2013;31:58-64.  Back to cited text no. 22
    
23.
Cobankara FK, Unlu N, Cetin AR, Ozkan HB. The effect of different restoration techniques on the fracture resistance of endodontically-treated molars. Oper Dent 2008;33:526-33.  Back to cited text no. 23
    
24.
Monga P, Sharma V, Kumar S. Comparison of fracture resistance of endodontically treated teeth using different coronal restorative materials: An in vitro study. J Conserv Dent 2009;12:154-9.  Back to cited text no. 24
[PUBMED]  [Full text]  
25.
Ehlers V, Gran K, Callaway A, Azrak B, Ernst CP. One-year clinical performance of flowable bulk-fill composite vs. conventional compomer restorations in primary molars. J Adhes Dent 2019;21:247-54.  Back to cited text no. 25
    
26.
Oter B, Deniz K, Cehreli SB. Preliminary data on clinical performance of bulk-fill restorations in primary molars. Niger J Clin Pract 2018;21:1484-91.  Back to cited text no. 26
[PUBMED]  [Full text]  
27.
Taha NA, Maghaireh GA, Ghannam AS, Palamara JE. Effect of bulk-fill base material on fracture strength of root-filled teeth restored with laminate resin composite restorations. J Dent 2017;63:60-4.  Back to cited text no. 27
    



 
 
    Tables

  [Table 1]



 

Top
 
 
Search
Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
Access Statistics
Email Alert *
Add to My List *
* Registration required (free)  

 
  In this article
Abstract
Introduction
Materials and Me...
Results
Discussion
Conclusion
References
Article Tables

 Article Access Statistics
    Viewed594    
    Printed12    
    Emailed0    
    PDF Downloaded119    
    Comments [Add]    

Recommend this journal